资源描述
单击此处编辑母版标题样式,单击此处编辑母版文本样式,第二级,第三级,第四级,第五级,*,Tangshan Polar Bear Co. Ltd,HCSA / HCSAF,超高强水泥在自流平砂浆中的应用,Application of HCSA / HCSAF Binder in Self-leveling Flooring Material,Alex Yin,HCSA / HCSAF,超高强水泥,What is HCSA/HCSAF Binder?,特殊煅烧的硫铝酸盐水泥 /高铁硫铝酸盐水泥,不同于普通的硫铝酸盐水泥,不同于铝酸盐水泥和硅酸盐水泥,主要矿物相 Major Mineral Phase,C,4,AF,次要矿物相 Minor phases,C,2,S,f-CaSO,4,无游离氧化钙、无铝酸钙相 no free lime, no C,12,A,7,or C,3,A,水化 Hydration,外加的石膏量左右着所形成的钙钒石的数量，从而影响系统最终的物理化学性能,The amount of calcium sulphate added affect the quantity of AFt formed, thus influencing the characteristics of the final system,特性 Characteristics,快凝 Fast Setting,快硬 Rapid Hardening,高强 High Early Strength,补偿收缩 Shrinkage Compensation,自枯燥 Self Drying,自养护 Self Curing,低温施工 Low temperature Application,制备过程Manufacturing process,铝矾土,石灰石,石膏,球磨机,回转窑,掺合料（可选）,HCSA超高强水泥,HCSAF超高强水泥,HCSA/HCSAF超高强水泥与 OPC、CAC 的熟料化学分析及矿物相比照,HCSA,HCSAF,国外CAC,OPC,CaO,3941,4043,36.539.5,6467,Al,2,O,3,3540,3237,37.541.5,48,SiO,2,4.56.5,4.56.5,2.55,2125,Fe,2,O,3,+FeO,13,510,1418,24,SO,3,911,710,-,-,Major Phases,C,4,AF,CA,C,4,AF,C,3,S 4260,C,2,S 1535,C,3,A 514,C,4,AF 1016,HCSA, HCSAF，CAC, OPC,HCSA,HCSAF,国外CAC,OPC,系统,C-A-S-,S,C-A-S-F-,S,C-S-A,C-S-A-F,主要矿物,C,4,A,3,S,C,4,A,3,S,C,4,AF,CA,C,4,AF,C,3,S, C,2,S,次要矿物,C,2,S,C,2,S,C,12,A,7, C,2,AS,C,3,A, C,4,AF,凝结,13h,13h,23h,23h,硬化,快,快,快,慢,水化产物,AFt,AH,3,CSH,AFt,AH,3,FH,3,CSH,C-A(F)-H, AH,3,FH,3,CSH,CH,早期强度,高,高,高,低,不同类型水泥的性能比较 Comparative properties of different types of cement,强度发展速率,Strength Development rate,放热速率,Rate of heat evolution,补偿收缩开裂的能力,Resistance to Shrinkage cracking,抵抗化学侵蚀的能力,Inherent Resistance to chemical attack,硫酸盐,弱酸,快硬硅酸盐水泥,(RHPC),高,高,低,低,低,普通硅酸盐水泥,(OPC),低,低,低,低,低,低热硅酸盐水泥,(Low Heat PC),很低,很低,低,低,低,铝酸盐水泥,(CAC),很高,很高,高,很高,高,HCSA超高强水泥,很高,很高,高,很高,高,HCSAF超高强水泥,很高,很高,高,很高,高,在干混砂浆中的应用,Application in Dry Mix Mortar,堵漏材料,Water stopping mortar,自流平,Self Levelling compounds,无收缩灌浆材料,Non-shrinking grouts,修补砂浆,Repair mortars,瓷砖胶粘剂,Tile Adhesives,加固材料,soil solidification material,自流平砂浆Self levelling compounds,适用于建筑物地面，尤其是适用于作为工业厂房地坪与家居装修室内地面的找平层 、面层,For levelling of uneven substrates either as underlayment or as overlayment,特别地当要在很短时间或周末进行装新或修复工程时,Especially when renovation or repairing work has to be done in short time or over the weekends,自流平砂浆的根本要求Fundamental requirements for SLC,很好的流动性,增强的外表硬度和耐磨性能,很好的粘结强度和力学性能,无泌水和沉降 (浆体的高度稳定性能),不发生收缩开裂,Very good flow,Enhanced surface hardness and abrasion resistance,Good bond and compressive strength,No bleeding or segregation (good stabilisation of suspension),No occurrence of shrinkage cracking,自流平组成SLC composition,胶凝材料,OPC,CAC / HCSA /HCSAF,CaSO4,骨料 aggregate,填料 filler,添加剂 addtitive,胶凝材料,Cementitious material,现行技术,Current technology,OPC + CAC + Gypsum,以硅酸盐水泥为基,CAC +,OPC +,Gypsum,以铝酸盐水泥为基,利用,HCSA/HCSAF,的自流平技术,Cementitious,SLC using HCSA/HCSAF,OPC + HCSA/HCSAF + Gypsum,HCSA/HCSAF +,OPC +,Gypsum,与 OPC的复合,Mixing With OPC,要引起注意的 OPC 的几个性能,细度,C,3,A 含量,掺合料含量和类型,对于所用的OPC，必须进行复配试验,所用石膏的类型,添加剂,Additives,用于 Used for,调整凝结时间adjust setting time,控制水化control hydration process,改善流变行为modify rheology behavior,提高机械强度enhance mechanical performance,可以使用的化学添加剂有,聚合物，或者是胶粉，或者是乳液polymer,消泡剂defoamer,缓凝剂retarder,促凝剂accelerator,塑化剂/超塑化剂减水剂Plasticizer / SP,流变改性剂rheology modifier,纤维fiber,通过对组分的适中选择和控制，可以到达：,可调凝结时间,适于施工的流变性能,高早强,高的长龄期强度,补偿收缩,With a proper control of constituents, it is possible to get,Adjustable setting time,Rheology adapted to the application,High early strength,High long term strength,Shrinkage compensation,利用HCSA/HCSAF自流平砂浆的性能,施工速度快 - 一天内可对地面进行大面积的处理；,早强高强性能 - 强度开展快，加快施工进度,较高的粘结强度-与基底砼接合紧密，不易空鼓；,易施工 - 工厂预包装材料，操作简单，现场只需加水搅拌即可施工，高流动性能保证了现场很容易进行搅拌以及材料的一致性和均匀性；也可泵送施工。,体积稳定 - 具有很低的收缩率，可以进行大面积的无缝施工；,耐久性 -良好的抗渗和耐腐蚀能力 。,经济 - 具有更高的性价比,快速强度增长Rapid Strength Gain,2小时上人,面层24小时可上轻载,Walk-on time in two hours,Light traffic in 24 hours for Overlay,补偿收缩,Shrinkage compensation,Allows large seamless areas to be installed,Must follow existing substrate joints,水中膨胀,Wet Expansion,HCSA和国外CAC性能比照- 抗压强度,OPC-CAC-C,S,系统中，其余组分相同，但用HCSA等量替代国外CAC,1d抗压强度HCSA高于国外CAC,28d强度HCSA与国外CAC相当,HCSA和国外CAC性能比照- 干缩,OPC-CAC-C,S,系统中，其余组分相同，但用HCSA等量替代国外CAC,HCSA和国外CAC的收缩都很低,无论早期还是后期，国外CAC的干缩均比HCSA稍大,HCSA和HCSAF性能比照- 抗压强度,HCSA-C,S,-OPC系统中，其余组分相同，但用HCSAF等量替代HCSA,早期和长龄期强度HCSAF均稍高于HCSA,HCSA和HCSAF性能比照- 干缩,HCSA-C,S,-OPC系统中，其余组分相同，但用HCSAF等量替代HCSA,早期和长龄期干缩HCSAF均低于HCSA,稳定性以HCSAF为例,OPC-HCSAF-C,S,系统中，组分相同，但用不同批号的HCSAF,流动性,抗压强度,干缩,应用 Application,作为环氧树脂、PU等的垫层找平材料，如,食品加工厂,医药生产车间,电子设备车间,汽车制造车间或维修车间,基础混凝土,水泥自流平材料,环氧树脂、PU等（薄涂、平涂）,应用,作为PVC、瓷砖、地毯、木板等的根底找平材料，如,办公室,公寓、民用住房,百货店、超市,医院,基础混凝土,水泥自流平材料,PVC、瓷砖等,应用,作为耐磨面层材料， 如,工厂,地下车库,仓储、库房,展厅,基础混凝土,水泥自流平材料,自流平面,层,应用,作为彩色装饰面层材料， 如,办公室,展厅,百货店、超市,基础混凝土,水泥自流平材料,彩色自流平面层,结论Conclusion,利用HCSA/HCSAF超高强水泥能成功地开发出低本钱、高性能的自流平面层和垫层；,HCSA/HCSAF超高强水泥能够在自流平砂浆中完全替代国外的铝酸盐水泥；,利用HCSA/HCSAF超高强水泥配制自流平砂浆需要严格选择所用硅酸盐水泥，以及所用石膏的类型。,联系我们,展览中心1号馆1A718,殷庆立,唐山北极熊特种水泥有限责任公司,Tel：,Fax: 0315-7536201,Thank you !,
展开阅读全文