资源描述
1. Scope This Japanese Industrial Standard specifies the carbon steel tubes, hereinafter referred to as the tubes, used for machinery, automobiles, bicycles, furniture, appliances and other machine parts. Remark1. The units and numerical values given in in this Standard are based on the International System of Units (SI) and are appended for informatibe reference.2. Further, the traditional units accompanied by numerical values in this Standard shall be converted to the SI units and numerical values on January 1. 1991.2. Grade and DesignationThe grade and designation of the tube shall be as given in Table 1.The subclassification letter symbols A, B and C are used to indicate distinction of method of manufacturing the tube, cold working process, heat treatment, etc.Table 1. Grade and DesignationGrade DEsignation Grade 11 A STKM 11A Grade 12 A STKM 12A B STKM 12B C STKM 12C Grade 13 A STKM 13A B STKM 13B C STKM 13C Grade 14 A STKM 14A B STKM 14B C STKM 14C Grade 15 A STKM 15A C STKM 15C Grade 16 A STKM 16A C STKM 16C Grade 17 A STKM 17A C STKM 17C Grade 18 A STKM 18A B STKM 18B C STKM 18C Grade 19 A STKM 19A C STKM 19C Grade 20 A STKM 20A * World Standard Comparative Table KS ASTM JIS BS NUBER GRADE NUBER GRADE NUBER GRADE NUBER GRADE D 3517 Grade 11 A STKM 11 A A513A519 MT1010MT1010 G-3445 STKM11A - - Grade 12A STKM 12 A A513A519 MT1015MT1015 STKM12A 980 CDS-3 Grade 12 B STKM 12 B - - STKM12B - - Grade 12C STKM 12C A512A513 MT1015 STKM12C - - Grade 13 A STKM 13 A A512A513A519 MT 1025MTX1025MT 1025 STKM13A - - Grade13B STKM 13 B - - STKM13B 980 CDS-4 Grade13 C STKM 13 C - - STKM13C - - Grade14 A STKM 14 A A513A519 MT1030MT1030 STKM14A 1717 CDS-103 Grade14 B STKM 14 B - - STKM14B - - Grade14 C STKM 14 C - - STKM14C - - Grade15 A STKM 15 A A513 MT1033 STKM15A 1717 CDS-105 Grade15 C STKM 15 C - - STKM15C - - Grade16 A STKM 16 A A519 MT1040 STKM16A 980 CDS-5 Grade16 C STKM 16 C - - STKM16C - - Grade17 A STKM 17 A A519 MT1050 STKM17A 9801717 CDS-7CDS-107 Grade17 C STKM 17 C - - STKM17B - - Grade18 A STKM 18 A A519 MT1524 STKM18A 980 CDS-9 Grade18 B STKM 18 B - - STKM18B - - Grade18 C STKM 18 C - - STKM18C - - Grade19 A STKM 19 A - - - - - Grade19 C STKM 19 C - - - - - Grade20 A STKM 20 A - - - - - - - - A512 MT1008 - - - - - - - A512A519 MTX1020MTX1020 - - - - - - - A512A519 MTX1015MTX1015 - - - - - - - A512A513A519 MT1008MT1008MT1008 - - - - - - - A512A513 MT1010MT1010 - - - - - - - A512A513A519 MT1012MT1012MT1012 - - - - - - - A512 MT1015 - - - - - - - A512A513A519 MT1016MT1016MT1016 - - - - - - - A512A513A519 MT1018MT1018MT1018 - - - - - - - A512A513A519 MT1019MT1019MT1019 - - - - - - - A512A513A519 MT1021MT1021MT1021 - - - - - - - A512A513A519 MT1026MT1026MT1026 - - - - - - - A512A513A519 MT1035MT1035MT1035 - - - - - - - A512 MT1100 - - - - - - - A512 MT1115 - - - - - - - A512 MT1117 - - - - - - - A513A519 MT1017MT1017 - - - - - - - A513A519 MT1022MT1022 - - - - - - - A513A519 MT1023MT1023 - - - - - - - A513A519 MT1024MT1024 - - - - - - - A513A519 MT1050MT1050 - - - - - - - A513 MT1060 - - - - - - - A513 MT1340 - - - - - - - A513A519 MT1524MT1524 - - - - - - - A513 MT4118 - - - - - - - A513 MT4130 - - - - - - - A513 MT4140 - - - - - - - A513 MT5130 - - - - - - - A513 MT8620 - - - - - - - A513 MT8630 - - - - - - - A519 MT1524 - - - - - - - A519 MT1541 - - - - 3. Method of Manufacture3.1 The tubes of Grades 11, 12 and 13 shall be manufactured by seamless process, electric resistance welding process, or butt welding process, and those of other grades shall be manufactured by seamless process or electric resistance welding process. 3.2 The tube shall be as manufactured or as cold-finished condition, or they shall be subjected to appropriate heat treatment.4.Chemical Composition4. Chemical CompositionThe tube shall be tested in accordance with 8.1 and the resulting ladle analysis values shall conform to Table 2.Table 2. chemical Compositon Grade Designation Unit % C Si Mn P S Nb or V Grade 11 A STKM 11A 0.12 max. 0.35 max. 0.60 max. 0.040 max. 0.040 max. - Grade 12 A STKM 12A 0.20 max. 0.35 max. 0.60 max. 0.040 max. 0.040 max. - B STKM 12B C STKM 12C Grade 13 A STKM 13A 0.25 max. 0.35 max. 0.300.90 0.040 max. 0.040 max. - B STKM 13B C STKM 13C Grade 14 A STKM 14A 0.30 max. 0.35 max. 0.301.00 0.040 max. 0.040 max. - B STKM 14B C STKM 14C Grade 15 A STKM 15A 0.250.35 0.35 max. 0.301.00 0.040 max. 0.040 max. - C STKM 15C Grade 16 A STKM 16A 0.350.45 0.40 max. 0.401.00 0.040 max. 0.040 max. - C STKM 16C Grade 17 A STKM 17A 0.450.55 0.40 max. 0.401.00 0.040 max. 0.040 max. - C STKM 17C Grade 18 A STKM 18A 0.18 max. 0.55 max. 1.50 max. 0.040 max. 0.040 max. - B STKM 18B C STKM 18C Grade 19 A STKM 19A 0.25 max. 0.55 max. 1.50 max. 0.040 max. 0.040 max. - C STKM 19C Grade 20 A STKM 20A 0.25 max. 0.55 max. 1.60 max. 0.040 max. 0.040 max. 0.15 max. Remarks1. When the purchaser requires product analyssis for the tubes made of killed steel, the tolerances for the values given above shall be as specified in Table 2 in JIS G 0321 for seamless steel tubes and in Table 1 for electric resistance welded or butt welded steel tubes.2. For the tubes of Grade 15 made by electric resistance welding process, the lower limit of carbon content may be altered by agreement between the parties concerned.3. For the tubes of Grade 20, Nb in combination with V may be added. In this case, the maximum content of Nb + V shall be 0.15 %. 5 Mechanical Properties5. Mechanical Properties5.1 Tensile Strength, Yield Point or Proof Stress, and ElongationThe tube shall be tested in accordance with 8.2 and the resulting tensile strength, yield point or proof stress, and elongation shall comply with Table 35.2 Bending Strength or Flattening StrengthThe tube shall be tested in accordance with 8.3 or 8.4 and shall be free from flaws or cracks on their wall surfaces.The bending test, however, shall be applied to the tubes 50 mm or under in outside diameter in lieu of flattening test when especially specified by the purchaser.Grade Designation Tensile strengthN/kgf/ Yield point or proofN/kgf/Elongation % Flattening strength Bending strength No. 4, No. 11 No. 12 test pieces Longitudinal direction No. 4, No. 5 test pieces Transverse direction Distance between flat plates (H)(D is outside dia. of the tube) Bend angle Inside radius (D is outside dia. of the tube) 11辆 A STKM11A 29030 min. - 35 min. 30 min. 1/2 D 180 4 D 12辆 A STKM12A 34035 min. 17518 min. 35 min. 30 min. 2/3 D 90 6 D B STKM12B 39040 min. 27528 min. 25 min. 20 min. 2/3 D 90 6 D C STKM12C 47048 min. 35536 min. 20 min. 15 min. - - - 13辆 A STKM13A 37038 min. 21522 min. 30 min. 25 min. 2/3 D 90 6 D B STKM13B 44045 min. 30531 min. 20 min. 15 min. 3/4 D 90 6 D C STKM13C 51052 min. 38039 min. 15 min. 10 min. - - - 14辆 A STKM14A 41042 min. 24525 min. 25 min. 20 min. 3/4 D 90 6 D B STKM14B 50051 min. 35536 min. 15 min. 10 min. 7/8 D 90 8 D C STKM14C 55056 min. 41042 min. 15 min. 10 min. - - - 15 辆 A STKM15A 47048 min. 27528 min. 22 min. 17 min. 3/4 D 90 6 D C STKM15C 58059 min. 43044 min. 12 min. 7 min. - - - 16辆 A STKM16A 51052 min. 32533 min. 20 min. 15 min. 7/8 D 90 8 D C STKM16C 62063 min. 46047 min. 12 min. 7 min. - - - 17 辆 A STKM17A 55056 min. 34535 min. 20 min. 15 min. 7/8 D 90 8 D C STKM17C 65066 min. 48049 min. 10 min. 5 min. - - - 18辆 A STKM18A 44045 min. 27528 min. 25 min. 20 min. 7/8 D 90 6 D B STKM18B 49050 min. 31532min. 23 min. 18 min. 7/8 D 90 8 D C STKM18C 51052 min. 38039 min. 15 min. 10 min. - - - 19辆 A STKM19A 49050 min. 31532 min. 23 min. 18 min. 7/8 D 90 6 D C STKM19C 55056 min. 41042 min. 15 min. 10 min. - - - 20辆 A STKM20A 54055 min. 39040 min. 23 min. 18 min. 7/8 D 90 6 D RemarksWhen the tensile test is carried out on No. 12 or No. 5 test piece for the tube under 8 mm in wall thickness, the minimum value of elongation shall be calculated by subtracting 1.5 % from the values of elongation given in Table 3 for each 1 mm decrease in wall thickness and rounding off to an integer in accordanc with JIS Z 0 8401. Examples of calculation are given in Referene Table.2. The values of elongation in Table 3 shall not be applied to the these 40 mm or smaller in outside diameter.However, it may be agreed upon by the purchaser and the manufacturer. when especially reequired.3. For electric resistance welded steel tubes ad butt-welded steel tubes.the tensile test pieces shall be No. 12 or No. 5 and they shall be taken from a portion not involving welded seems4. For the flattening test, the minimum distance between the flat plates (H) shall be 5 times the plate thickness. 6. Apperance6.1 The tubes shall be practically straight. and the two ends shall be at right angles to the axis of the tube.6.2 The tubes shall be free from defects detrimental to pactical use.6.3 The surface finish of the tubes, when especially specified shall be agreed upon by the purchaser and the manufacturer.7. Dimensional Tolerances7. Dimensional Tolerances7.1 The tolerances on outside diameter and wall thickness for the tubes shall be as given in Table 4 and Table 5, respectively .Table 4. Tolerances on Outside Diameter Division Tolerances on outside diameter No. 1 Under 50mm【0.5mm50mm or over 【1% No. 2 Under 50mm 【0.25mm50mm or over 【0.5% No. 3 Under 25mm 【0.12mm25mm or over to and excl. 40mm 【0.15mm40mm or over to and excl.50mm 【0.18mm50mm or over to and excl.60mm 【0.20mm60mm or over to and excl.70mm 【0.23mm70mm or over to and excl.80mm 【0.25mm80mm or over to and excl.90mm 【0.30mm90mm or over to and excl.100mm 【0.40mm100mm or over 【0.50% Remarks 1.For hot finished seamless steel tube, the outside diameter tolerances No. 1 shall be applied.2.The tolerances on outside diameter of quenched and tempered tubes shall be as agreed upon by the purchaser and the manufacturer.Table 5. Tolerances on Wall ThicknessDivision Tolerances on wall thickness No. 1 Under 4mm +0.6mm-0.5mm 4mm or over+15% -12.5% N. 2 Under 3mm 【0.3mm 3mm or over 【10% No. 3 Under 2mm 【0.15mm 2mm or over【8% Remarks For hot finished seamless steel tubes the tplerances NO. 1 shall be applied.7.2 The tolerances on the tube length shall be in the range of 0 to + 50 mm. However, when tolerances outside this range are especially required, agreement shall be made between the purchaser and the manufacturer. 8. Test 8.1 Chemiacl Analysis 8.1.1 Chemical analysisThe general requirements for chemical analysis and method of sampling specimens for analysis shall be in accordance with the 3. in JIS G 03038.1.2 Analytical MethodThe analytical method shall be in accordance with one of thefollowing Standards. JIS G 1211. JIS G 1212, JIS G 1213, JIS G 1214, JIS G 1215,JIS G 1221, JIS G 1237, JIS G 1243, JIS G 1256, JIS G 1257.8.2 Tensile Test 8.2.1 Test PieceThe test piece shall be No. 11, No. 12 A, No. 12 B, No. 12 C, No. 4 or No. 5 test piece specified in JIS Z 2201 and shall be cut off from the tube. The gauge length for No. 4 test piece, however, shall be 50 mm8.2.2 Test Method The test method shall be in accordance with JIS Z 2241.8.3 Bending Test8.3.1 Test PieceA suitable length of a tube shall be cut off from oneend of the tube to be made into a test piece. 8.3.2 Test MethodThe test piece shall be bent, at ordinary temperature around a cylinder with the bend angle and inside radius specified in Table 3 and checked for the occurrence of flaws or cracks. In the case of electric resistance welded steel tubes and butt-welded steel tubes, the weld shall be placed in the outermost part of the bent portion8.4 Flattening Test 8.4.1 Test Piece A test piece 50mm or over in length shall be cut off from one end of a tube. For the tube of wall thickness 15 % or over of its outside diameter, a test piece made into C-shape by removing part of the circumference of a full-section test piece may be used.8.4.2 Test MethodThe test piece shall be placed between two flat plates, flattened by compression at ordinary temperature until the distance between the plates comes to the specified in Table 3, and checked for the tance welded steel tubesand butt-welded steel tubes, the weld shall be placed at right angles to the direction of compression as shown in Fig. 1. Further, a C-shape test piece shall be placed as shown in Fig. 2.Fig 1. Flattning Test (for Full-section Test Piece)Fig 2. Flattening Test (for C-shape Test Piece)9. Inspection9.1 InspectionThe general requirements for inspection shall be in accordance with JIS G 0303.9.2The chemical composition, mechanical properties, dimensions and apperance shall conform to the requirenments specified in 3., 4., 5. and 6. the bending test and the flattening test, however, may be omitted when approved by the purchaser.9.3 The purchaser may specify a flaring test, hydrostatictest, etc., in addition to those specified in 9.2 In this case, the test items, sampling method and acceptance criteria shall be previously agreed upon by the manufacturer.9.4 The numver of specimens for product analysis shall be as agreed upon by the purchaser and the manufacturer.9.5 The method of sampling specimens and the number of test pieces for tensile test, bending test and flattening test shall be as given in Table 6.Table 6. Method of Sampling Specimens and Number of TEst Pieces.Grade Designation Division of outside diameter Method of sampling specimens and number of test pieces A and B of 11 to 20 STKM 11ASTKM 12ASTKM 12BSTKM 13ASTKM 13BSTKM 14ASTKM 14BSTKM 15ASTKM 16ASTKM 17ASTKM 18ASTKM 18BSTKM 19ASTKM 20A 100 mm or under Take one specimen from each 1000 m or its fraction of the tubes of the same dimensions. From the specimen, take one flattening or bend test piece for the tubes 50 mm or under in outside diameter, and one flattening test piece for the tubes over 50 mm in outside diameter, in addition to each one tensile test piece in either case. Over 100 mm up to and incl. 200 mm Take one specimen from each 500 m or its fraction of the tubes of the same dimensions. From the specimen, take one tensile test piece and one flattening test piece. Over 200 mm Take one specimen from each 250 m or its fraction of the tubes of the same dimensions. From the specimen, take one tenseil test piece and one flattening test piece. C of 12 to 19 STKM 12CSTKM 13CSTKM 14CSTKM 15CSTKM 16CSTKM 17CSTKM 18CSTKM 19C 100 mm or under Take one specimen from each 1000 m or its fraction of the tubes of the same dimensions. From the specimen, take one tensile test piece. Over 100 mm up to and incl. 200 mm Take one specimen from each 500 m or its fraction of the tubes of the same dimensions. From the specimen. take one tensile test piece. Over 200 mm Take one specimen from each 250 m or its fraction of the tubes of the same dimensions. From the specimen.take one tensile test piece10. ReinspectionThe tube may be retested in accordance with 4.4 in JIS G 0303.11.MarkingEach tube having passed the inspection shall be legibly marked with the following items, the order of arranging the items is not specified.However, for smaller tubes or on a request from the purchaser, tubes may be bundled together and marked for each bundle by suitable means. (1) Designation of grade(2) Letter symbol indicating the manufacturing process()Note (1)The letter symbol indicating the manufacturing process shall be as follows.However, the sign may be replaced by a blankHot finished seamless steel tube -S-HCold finished seamless steel tube -S-CElectric resistance welded steel tube other -E-Gthan hot finished or cold finished onesHot finished electric resistance welded steel tube -E-HCold finished electric resistance welded steel tube -BCold finished butt-welded steel tube -B-C12. ReportThe manufacturer shall, as a rule, submit to the purchaser a report on the test results,manufacturing process, ordered dimensions, quantity and work lot number traceable to the history of manufacture, etc. JIS Number and Corrensponding Foreign StandardsJISASTMBSDINNFISOIndex NumberStandard NumberGradeTupe Standard NumberGradeTupe Standard NumberGradeTupe Standard NumberGradeTupe Standard NumberGradeTupe Standard NumberGradeTupe G3445STKM11ACA512MT1010C1717ERWC1C2391St30SiC3304R28CC017A513MT1010CSt30A1C3305C2393St28C3306CRSt28C2394St28CUSt28CRSt28CSTKM12ACA512MT1015C1717ERWC2C2391St37-23304R33CA513MT1015C6323HFS3CRSt37-23305STKM12BCA512MT1015C2394St37-23306A513MT1015CUst38-2A519MT1015CRSt-2STKM12CC1717CEWC2CA49-322TU37bCCFSC3CA49-327
展开阅读全文